ULTRACOTE

(UP-5000)

A CLOSER LOOK AT ULTRACOTE

The following photomicrographs were prepared on an ElectroScan E-3 Environmental Scanning Electron Microscope (ESEM) at Western Research Institute (WRI) of Laramie, Wyoming. Since the early 1960's WRI has worked with the Federal Highway Administration to clarify the chemistry of petroleum asphalt to enhance performance in roadways.

Here is a look inside ULTRACOTE and its incredible properties:

These pictures produced by the ESEM have been color highlighted to make it easier to identify the subjects. The aggregate (stone) is blue, ULTRACOTE is gold, and the asphalt oil is black. The first ESEM photomicrograph shows the surface of aggregate coated with asphalt (upper left). The white scale bar represents 50 microns. For comparison, a 270 mesh sieve has an opening of 53 microns or .0021 inches.

The next ESEM photomicrograph is of the surface of aggregate coated with ULTRACOTE (middle left). The white scale bar represents 50 microns. The largest stone is about 250 microns (60 mesh sieve size) and the other five large stones are about 100-125 microns (120-140 mesh sieve size).

This last photomicrograph (lower left) shows the outer edge of a cross-section of aggregate that was coated with 0.1% ULTRACOTE, then coated with asphalt.
During this exposure an electron beam was focused on these three components to determine their reaction to the heat of the beam. The asphalt began to flow after a few minutes as depicted by the ropy looking texture. The ULTRACOTE appears to be unaffected by the electron beam's heat.

* Complete technical details are available through our regional offices.

Next Page || Home Page || Products

	These pictures produced by the ESEM have been color highlighted to make it easier to identify the subjects. The aggregate (stone) is blue, ULTRACOTE is gold, and the asphalt oil is black. The first ESEM photomicrograph shows the surface of aggregate coated with asphalt (upper left). The white scale bar represents 50 microns. For comparison, a 270 mesh sieve has an opening of 53 microns or .0021 inches.
	The next ESEM photomicrograph is of the surface of aggregate coated with ULTRACOTE (middle left). The white scale bar represents 50 microns. The largest stone is about 250 microns (60 mesh sieve size) and the other five large stones are about 100-125 microns (120-140 mesh sieve size).
	This last photomicrograph (lower left) shows the outer edge of a cross-section of aggregate that was coated with 0.1% ULTRACOTE, then coated with asphalt. During this exposure an electron beam was focused on these three components to determine their reaction to the heat of the beam. The asphalt began to flow after a few minutes as depicted by the ropy looking texture. The ULTRACOTE appears to be unaffected by the electron beam's heat.